Element

Linear Thermal Expansion Coefficient

Click button to see citations

Notes

Aluminum

25 °C

23.1×10-6 K-1   

293 K

22.9×10-6 K-1   

283 K

22.42×10-6 K-1  

85 K

 9.87×10-6 K-1  

75 K

 8.18×10-6 K-1  

65 K

 6.32×10-6 K-1  

57.5 K

 5.03×10-6 K-1  

34 K

 1.249×10-6 K-1 

32 K

 1.037×10-6 K-1 

30 K

 0.841×10-6 K-1 

28 K

 0.670×10-6 K-1 

26 K

 0.525×10-6 K-1 

24 K

 0.406×10-6 K-1 

22 K

 0.309×10-6 K-1 

20 K

 0.232×10-6 K-1 

18 K

 0.1704×10-6 K-1

16 K

 0.1223×10-6 K-1

14 K

 0.0850×10-6 K-1

12 K

 0.0567×10-6 K-1

10 K

 0.0359×10-6 K-1

9 K

 0.0278×10-6 K-1

8 K

 0.0212×10-6 K-1

7 K

 0.0158×10-6 K-1

6 K

 0.0114×10-6 K-1

5 K

 0.0081×10-6 K-1

4 K

 0.0055×10-6 K-1

3 K

 0.0035×10-6 K-1

2 K

 0.0021×10-6 K-1

1 K

 0.0009×10-6 K-1

Antimony

25 °C

11.0×10-6 K-1   

Barium

25 °C

20.6×10-6 K-1   

Beryllium

25 °C

11.3×10-6 K-1   

Bismuth

25 °C

13.4×10-6 K-1   

Cadmium

25 °C

30.8×10-6 K-1   

Calcium

25 °C

22.3×10-6 K-1   

Carbon

graphite

400 °C

28×10-6 K-1     

c direction

0 °C

25×10-6 K-1     

c direction

Cerium

25 °C

 6.3×10-6 K-1   

Cesium

25 °C

97×10-6 K-1     

Chromium

25 °C

 4.9×10-6 K-1   

Cobalt

25 °C

13.0×10-6 K-1   

Copper

25 °C

16.5×10-6 K-1   

293 K

16.65×10-6 K-1  

283 K

16.43×10-6 K-1  

85 K

 8.94×10-6 K-1  

75 K

 7.69×10-6 K-1  

65 K

 6.26×10-6 K-1  

57.5 K

 5.09×10-6 K-1  

34 K

 1.48×10-6 K-1  

32 K

 1.23×10-6 K-1  

30 K

 1.01×10-6 K-1  

28 K

 0.815×10-6 K-1 

26 K

 0.640×10-6 K-1 

25 K

 0.564×10-6 K-1 

24 K

 0.494×10-6 K-1 

22 K

 0.372×10-6 K-1 

20 K

 0.271×10-6 K-1 

18 K

 0.192×10-6 K-1 

16 K

 0.1310×10-6 K-1

15 K

 0.1070×10-6 K-1

14 K

 0.0865×10-6 K-1

12 K

 0.0530×10-6 K-1

10 K

 0.0310×10-6 K-1

9 K

 0.0229×10-6 K-1

8 K

 0.0164×10-6 K-1

7 K

 0.0113×10-6 K-1

6 K

 0.0075×10-6 K-1

5 K

 0.0046×10-6 K-1

4 K

 0.0027×10-6 K-1

3.5 K

 0.0020×10-6 K-1

3.0 K

 0.0014×10-6 K-1

2.5 K

 0.0009×10-6 K-1

2.0 K

 0.0006×10-6 K-1

Dysprosium

25 °C

 9.9×10-6 K-1   

Erbium

25 °C

12.2×10-6 K-1   

Europium

25 °C

35.0×10-6 K-1   

Gadolinium

100 °C

 9.4×10-6 K-1   

Gallium

25 °C

18×10-6 K-1     

Germanium

300 K

 5.9×10-6 K-1   

100 K

 2.2×10-6 K-1   

Gold

25 °C

14.2×10-6 K-1   

283 K

14.08×10-6 K-1  

85 K

11.03×10-6 K-1  

75 K

10.41×10-6 K-1  

65 K

 9.58×10-6 K-1  

57.5 K

 8.75×10-6 K-1  

30 K

 3.97×10-6 K-1  

28 K

 3.51×10-6 K-1  

26 K

 3.05×10-6 K-1  

25 K

 2.83×10-6 K-1  

24 K

 2.59×10-6 K-1  

22 K

 2.14×10-6 K-1  

20 K

 1.71×10-6 K-1  

18 K

 1.31×10-6 K-1  

16 K

 0.950×10-6 K-1 

15 K

 0.785×10-6 K-1 

14 K

 0.642×10-6 K-1 

12 K

 0.401×10-6 K-1 

10 K

 0.228×10-6 K-1 

9 K

 0.166×10-6 K-1 

8 K

 0.116×10-6 K-1 

7 K

 0.078×10-6 K-1 

6 K

 0.0494×10-6 K-1

5 K

 0.0294×10-6 K-1

4 K

 0.0155×10-6 K-1

3.5 K

 0.0105×10-6 K-1

3.0 K

 0.0068×10-6 K-1

2.5 K

 0.0040×10-6 K-1

2.0 K

 0.0021×10-6 K-1

Hafnium

25 °C

 5.9×10-6 K-1   

Holmium

25 °C

11.2×10-6 K-1   

Indium

25 °C

32.1×10-6 K-1   

Iridium

25 °C

 6.4×10-6 K-1   

283 K

 6.65×10-6 K-1  

85 K

 3.90×10-6 K-1  

75 K

 3.43×10-6 K-1  

65 K

 2.88×10-6 K-1  

57.5 K

 2.37×10-6 K-1  

30 K

 0.42×10-6 K-1  

28 K

 0.335×10-6 K-1 

25 K

 0.220×10-6 K-1 

22 K

 0.132×10-6 K-1 

20 K

 0.090×10-6 K-1 

18 K

 0.0630×10-6 K-1

15 K

 0.0360×10-6 K-1

12 K

 0.0205×10-6 K-1

10 K

 0.0140×10-6 K-1

8 K

 0.0098×10-6 K-1

6 K

 0.0065×10-6 K-1

5 K

 0.0050×10-6 K-1

4 K

 0.0038×10-6 K-1

3 K

 0.0028×10-6 K-1

Iron

25 °C

11.8×10-6 K-1   

293 K

11.8×10-6 K-1   

Lanthanum

25 °C

12.1×10-6 K-1   

References    (Click the button next to a value above to see complete citation information for that entry)

Barron, T. H. K., and G. K. White. Heat Capacity and Thermal Expansion at Low Temperatures. New York: Kluwer Academic / Plenum Publishers, 1999.

Cohen, E. Richard, David R. Lide, and George L. Trigg, editors. AlP Physics Desk Reference, 3rd edition. New York: Springer-Verlag New York, Inc., 2003.

Collins, J. G., G. K. White, and C. A. Swenson. "The Thermal Expansion of Aluminum below 35 K." Journal of Low Temperature Physics, volume 10, number 1-2, 1973, pp. 69–77. doi:10.1007/BF00655242

Lide, David R., editor. CRC Handbook of Chemistry and Physics, 88th edition. Boca Raton, Florida: Taylor & Francis Group, 2008.

Pierson, Hugh O. Handbook of Carbon, Graphite, Diamond and Fullerenes. Park Ridge, NJ: Noyes Publications, 1993.

Shur, Michael. Physics of Semiconductor Devices. Englewood Cliffs, NJ: Prentice-Hall, Inc., 1990.

White, G. K., and A. T. Pawlowicz. "Thermal Expansion of Rhodium, Iridium, and Palladium at Low Temperatures." Journal of Low Temperature Physics, volume 2, number 5-6, 1970, pp. 631–639. doi:10.1007/BF00628279

White, G. K., and J. G. Collins. "Thermal Expansion of Copper, Silver, and Gold at Low Temperatures." Journal of Low Temperature Physics, volume 7, number 1-2, 1972, pp. 43–75. doi:10.1007/BF00629120