Element

Isobaric Molar Heat Capacity

Click button to see citations

Notes

Actinium

298.15 K, 1 bar

27.2 J/(mol K)  

Aluminum

298.15 K, 1 bar

24.20 J/(mol K) 

Antimony

298.15 K, 1 bar

25.23 J/(mol K) 

Argon

gas

1200 K

1 atm

20.79 J/(mol K) 

1 bar

20.79 J/(mol K) 

1000 K

1 atm

20.79 J/(mol K) 

1 bar

20.79 J/(mol K) 

780 K

1 atm

20.79 J/(mol K) 

1 bar

20.79 J/(mol K) 

680 K

1 atm

20.79 J/(mol K) 

1 bar

20.79 J/(mol K) 

580 K

1 atm

20.80 J/(mol K) 

1 bar

20.80 J/(mol K) 

490 K

1 atm

20.80 J/(mol K) 

1 bar

20.80 J/(mol K) 

440 K

1 atm

20.80 J/(mol K) 

1 bar

20.80 J/(mol K) 

390 K

1 atm

20.81 J/(mol K) 

1 bar

20.81 J/(mol K) 

340 K

1 atm

20.82 J/(mol K) 

1 bar

20.82 J/(mol K) 

300 K

1 atm

20.83 J/(mol K) 

1 bar

20.83 J/(mol K) 

295 K

1 atm

20.84 J/(mol K) 

1 bar

20.84 J/(mol K) 

285 K

1 atm

20.84 J/(mol K) 

1 bar

20.84 J/(mol K) 

275 K

1 atm

20.85 J/(mol K) 

1 bar

20.85 J/(mol K) 

270 K

1 atm

20.85 J/(mol K) 

1 bar

20.85 J/(mol K) 

245 K

1 atm

20.87 J/(mol K) 

1 bar

20.87 J/(mol K) 

220 K

1 atm

20.89 J/(mol K) 

1 bar

20.89 J/(mol K) 

195 K

1 atm

20.93 J/(mol K) 

1 bar

20.93 J/(mol K) 

176 K

1 atm

20.98 J/(mol K) 

1 bar

20.97 J/(mol K) 

166 K

1 atm

21.01 J/(mol K) 

1 bar

21.01 J/(mol K) 

156 K

1 atm

21.05 J/(mol K) 

1 bar

21.05 J/(mol K) 

150 K

1 atm

21.08 J/(mol K) 

1 bar

21.08 J/(mol K) 

140 K

1 atm

21.16 J/(mol K) 

1 bar

21.15 J/(mol K) 

130 K

1 atm

21.28 J/(mol K) 

1 bar

21.27 J/(mol K) 

120 K

1 atm

21.48 J/(mol K) 

1 bar

21.47 J/(mol K) 

110 K

1 atm

21.86 J/(mol K) 

1 bar

21.84 J/(mol K) 

liquid

87.29 K, 1 atm

43.08 J/(mol K) 

87.17 K, 1 bar

43.06 J/(mol K) 

86 K

1 atm

42.90 J/(mol K) 

1 bar

42.90 J/(mol K) 

84 K

1 atm

42.63 J/(mol K) 

1 bar

42.63 J/(mol K) 

Arsenic

298.15 K, 1 bar

24.64 J/(mol K) 

gray arsenic, 298.15 K, 1 bar

24.64 J/(mol K) 

Barium

298.15 K, 1 bar

28.07 J/(mol K) 

Beryllium

298.15 K, 1 bar

16.443 J/(mol K)

Bismuth

298.15 K, 1 bar

25.52 J/(mol K) 

Boron

298.15 K, 1 bar

11.087 J/(mol K)

Bromine

298.15 K, 1 bar

75.69 J/(mol K) 

Cadmium

298.15 K, 1 bar

26.020 J/(mol K)

Calcium

298.15 K, 1 bar

25.929 J/(mol K)

Carbon

graphite, 298.15 K, 1 bar

 8.517 J/(mol K)

diamond, 298.15 K, 1 bar

 6.113 J/(mol K)

Cerium

298.15 K, 1 bar

26.94 J/(mol K) 

Cesium

298.15 K, 1 bar

32.210 J/(mol K)

Chlorine

298.15 K, 1 bar

33.949 J/(mol K)

Chromium

298.15 K, 1 bar

23.35 J/(mol K) 

Cobalt

298.15 K, 1 bar

24.81 J/(mol K) 

Copper

298.15 K, 1 bar

24.440 J/(mol K)

Dysprosium

298.15 K, 1 bar

28.16 J/(mol K) 

Erbium

298.15 K, 1 bar

28.12 J/(mol K) 

Europium

298.15 K, 1 bar

27.66 J/(mol K) 

Fluorine

298.15 K, 1 bar

31.304 J/(mol K)

Gadolinium

298.15 K, 1 bar

37.03 J/(mol K) 

Gallium

298.15 K, 1 bar

26.03 J/(mol K) 

Germanium

298.15 K, 1 bar

23.222 J/(mol K)

Gold

298.15 K, 1 bar

25.418 J/(mol K)

Hafnium

298.15 K, 1 bar

25.73 J/(mol K) 

Helium

298.15 K, 1 bar

20.786 J/(mol K)

Holmium

298.15 K, 1 bar

27.15 J/(mol K) 

Hydrogen

gas

400.0 K

1 atm

29.33 J/(mol K) 

parahydrogen

1 bar

29.33 J/(mol K) 

parahydrogen

300.0 K

1 atm

29.93 J/(mol K) 

parahydrogen

1 bar

29.93 J/(mol K) 

parahydrogen

298.15 K, 1 bar

28.836 J/(mol K)

280.0 K

1 atm

30.23 J/(mol K) 

parahydrogen

1 bar

30.23 J/(mol K) 

parahydrogen

270.0 K

1 atm

30.43 J/(mol K) 

parahydrogen

1 bar

30.42 J/(mol K) 

parahydrogen

260.0 K

1 atm

30.64 J/(mol K) 

parahydrogen

1 bar

30.64 J/(mol K) 

parahydrogen

250.0 K

1 atm

30.89 J/(mol K) 

parahydrogen

1 bar

30.89 J/(mol K) 

parahydrogen

200.0 K

1 atm

32.40 J/(mol K) 

parahydrogen

1 bar

32.40 J/(mol K) 

parahydrogen

150.0 K

1 atm

32.69 J/(mol K) 

parahydrogen

1 bar

32.69 J/(mol K) 

parahydrogen

100.0 K

1 atm

27.07 J/(mol K) 

parahydrogen

1 bar

27.06 J/(mol K) 

parahydrogen

90.0 K

1 atm

25.34 J/(mol K) 

parahydrogen

1 bar

25.34 J/(mol K) 

parahydrogen

80.0 K

1 atm

23.74 J/(mol K) 

parahydrogen

1 bar

23.74 J/(mol K) 

parahydrogen

70.0 K

1 atm

22.44 J/(mol K) 

parahydrogen

1 bar

22.44 J/(mol K) 

parahydrogen

60.0 K

1 atm

21.59 J/(mol K) 

parahydrogen

1 bar

21.59 J/(mol K) 

parahydrogen

50.0 K

1 atm

21.25 J/(mol K) 

parahydrogen

1 bar

21.24 J/(mol K) 

parahydrogen

48.0 K

1 atm

21.23 J/(mol K) 

parahydrogen

1 bar

21.23 J/(mol K) 

parahydrogen

46.0 K

1 atm

21.23 J/(mol K) 

parahydrogen

1 bar

21.22 J/(mol K) 

parahydrogen

44.0 K

1 atm

21.23 J/(mol K) 

parahydrogen

1 bar

21.23 J/(mol K) 

parahydrogen

42.0 K

1 atm

21.25 J/(mol K) 

parahydrogen

1 bar

21.25 J/(mol K) 

parahydrogen

40.0 K

1 atm

21.28 J/(mol K) 

parahydrogen

1 bar

21.27 J/(mol K) 

parahydrogen

38.0 K

1 atm

21.33 J/(mol K) 

parahydrogen

1 bar

21.33 J/(mol K) 

parahydrogen

36.0 K

1 atm

21.41 J/(mol K) 

parahydrogen

1 bar

21.40 J/(mol K) 

parahydrogen

34.0 K

1 atm

21.51 J/(mol K) 

parahydrogen

1 bar

21.50 J/(mol K) 

parahydrogen

32.0 K

1 atm

21.63 J/(mol K) 

parahydrogen

1 bar

21.62 J/(mol K) 

parahydrogen

30.0 K

1 atm

21.79 J/(mol K) 

parahydrogen

1 bar

21.78 J/(mol K) 

parahydrogen

28.0 K

1 atm

22.02 J/(mol K) 

parahydrogen

1 bar

22.00 J/(mol K) 

parahydrogen

26.0 K

1 atm

22.33 J/(mol K) 

parahydrogen

1 bar

22.31 J/(mol K) 

parahydrogen

deuterium, 298.15 K, 1 bar

29.196 J/(mol K)

Indium

298.15 K, 1 bar

26.74 J/(mol K) 

Iodine

298.15 K, 1 bar

54.438 J/(mol K)

Iridium

298.15 K, 1 bar

25.10 J/(mol K) 

Iron

298.15 K, 1 bar

25.10 J/(mol K) 

Krypton

298.15 K, 1 bar

20.786 J/(mol K)

Lanthanum

298.15 K, 1 bar

27.11 J/(mol K) 

Lead

298.15 K, 1 bar

26.84 J/(mol K) 

Lithium

298.15 K, 1 bar

24.860 J/(mol K)

Lutetium

298.15 K, 1 bar

26.86 J/(mol K) 

Magnesium

298.15 K, 1 bar

24.869 J/(mol K)

Manganese

298.15 K, 1 bar

26.32 J/(mol K) 

α-manganese, 298.15 K, 1 bar

26.32 J/(mol K) 

β-manganese, 298.15 K, 1 bar

26.53 J/(mol K) 

γ-manganese, 298.15 K, 1 bar

27.57 J/(mol K) 

Mercury

323.15 K

300 MPa

27.728 J/(mol K)

250 MPa

27.732 J/(mol K)

200 MPa

27.736 J/(mol K)

150 MPa

27.741 J/(mol K)

100 MPa

27.746 J/(mol K)

50 MPa

27.751 J/(mol K)

0 MPa

27.756 J/(mol K)

318.15 K

300 MPa

27.754 J/(mol K)

250 MPa

27.758 J/(mol K)

200 MPa

27.762 J/(mol K)

150 MPa

27.767 J/(mol K)

100 MPa

27.771 J/(mol K)

50 MPa

27.777 J/(mol K)

0 MPa

27.782 J/(mol K)

313.15 K

300 MPa

27.781 J/(mol K)

250 MPa

27.785 J/(mol K)

200 MPa

27.789 J/(mol K)

150 MPa

27.793 J/(mol K)

100 MPa

27.798 J/(mol K)

50 MPa

27.803 J/(mol K)

0 MPa

27.808 J/(mol K)

308.15 K

300 MPa

27.808 J/(mol K)

250 MPa

27.812 J/(mol K)

200 MPa

27.816 J/(mol K)

150 MPa

27.820 J/(mol K)

100 MPa

27.825 J/(mol K)

50 MPa

27.830 J/(mol K)

0 MPa

27.835 J/(mol K)

303.15 K

300 MPa

27.836 J/(mol K)

250 MPa

27.839 J/(mol K)

200 MPa

27.843 J/(mol K)

150 MPa

27.848 J/(mol K)

100 MPa

27.852 J/(mol K)

50 MPa

27.857 J/(mol K)

0 MPa

27.862 J/(mol K)

298.15 K

300 MPa

27.864 J/(mol K)

250 MPa

27.868 J/(mol K)

200 MPa

27.872 J/(mol K)

150 MPa

27.876 J/(mol K)

100 MPa

27.880 J/(mol K)

50 MPa

27.885 J/(mol K)

0 MPa

27.890 J/(mol K)

293.15 K

300 MPa

27.893 J/(mol K)

250 MPa

27.896 J/(mol K)

200 MPa

27.900 J/(mol K)

150 MPa

27.904 J/(mol K)

100 MPa

27.909 J/(mol K)

50 MPa

27.914 J/(mol K)

0 MPa

27.919 J/(mol K)

liquid, 298.15 K, 1 bar

27.983 J/(mol K)

Molybdenum

298.15 K, 1 bar

24.06 J/(mol K) 

Neodymium

298.15 K, 1 bar

27.45 J/(mol K) 

Neon

298.15 K, 1 bar

20.786 J/(mol K)

Nickel

298.15 K, 1 bar

26.07 J/(mol K) 

Niobium

298.15 K, 1 bar

24.60 J/(mol K) 

Nitrogen

gas

1000 K, 1 bar

32.70 J/(mol K) 

900 K, 1 bar

32.10 J/(mol K) 

800 K, 1 bar

31.44 J/(mol K) 

700 K, 1 bar

30.76 J/(mol K) 

600 K, 1 bar

30.12 J/(mol K) 

550 K, 1 bar

29.84 J/(mol K) 

500 K, 1 bar

29.59 J/(mol K) 

450 K, 1 bar

29.40 J/(mol K) 

400 K, 1 bar

29.27 J/(mol K) 

350 K, 1 bar

29.20 J/(mol K) 

340 K, 1 bar

29.19 J/(mol K) 

330 K, 1 bar

29.18 J/(mol K) 

320 K, 1 bar

29.18 J/(mol K) 

310 K, 1 bar

29.17 J/(mol K) 

300 K, 1 bar

29.17 J/(mol K) 

290 K, 1 bar

29.17 J/(mol K) 

280 K, 1 bar

29.17 J/(mol K) 

270 K, 1 bar

29.17 J/(mol K) 

260 K, 1 bar

29.18 J/(mol K) 

250 K, 1 bar

29.18 J/(mol K) 

240 K, 1 bar

29.19 J/(mol K) 

230 K, 1 bar

29.20 J/(mol K) 

220 K, 1 bar

29.21 J/(mol K) 

210 K, 1 bar

29.22 J/(mol K) 

200 K, 1 bar

29.23 J/(mol K) 

190 K, 1 bar

29.25 J/(mol K) 

180 K, 1 bar

29.27 J/(mol K) 

170 K, 1 bar

29.29 J/(mol K) 

160 K, 1 bar

29.33 J/(mol K) 

150 K, 1 bar

29.37 J/(mol K) 

145 K, 1 bar

29.40 J/(mol K) 

140 K, 1 bar

29.43 J/(mol K) 

135 K, 1 bar

29.46 J/(mol K) 

130 K, 1 bar

29.50 J/(mol K) 

125 K, 1 bar

29.55 J/(mol K) 

120 K, 1 bar

29.61 J/(mol K) 

115 K, 1 bar

29.68 J/(mol K) 

110 K, 1 bar

29.77 J/(mol K) 

105 K, 1 bar

29.88 J/(mol K) 

100 K, 1 bar

30.01 J/(mol K) 

95 K, 1 bar

30.19 J/(mol K) 

90 K, 1 bar

30.41 J/(mol K) 

85 K, 1 bar

30.72 J/(mol K) 

80 K, 1 bar

31.15 J/(mol K) 

77.244 K, 1 bar

31.46 J/(mol K) 

liquid

77.244 K, 1 bar

57.17 J/(mol K) 

75 K, 1 bar

56.89 J/(mol K) 

70 K, 1 bar

56.42 J/(mol K) 

65 K, 1 bar

56.11 J/(mol K) 

63.170 K, 1 bar

56.02 J/(mol K) 

Osmium

298.15 K, 1 bar

24.7 J/(mol K)  

Oxygen

gas

300 K

1 atm

29.44 J/(mol K) 

1 bar

29.43 J/(mol K) 

295 K

1 atm

29.41 J/(mol K) 

1 bar

29.41 J/(mol K) 

285 K

1 atm

29.37 J/(mol K) 

1 bar

29.37 J/(mol K) 

275 K

1 atm

29.34 J/(mol K) 

1 bar

29.34 J/(mol K) 

270 K

1 atm

29.32 J/(mol K) 

1 bar

29.32 J/(mol K) 

250 K

1 atm

29.28 J/(mol K) 

1 bar

29.28 J/(mol K) 

225 K

1 atm

29.26 J/(mol K) 

1 bar

29.25 J/(mol K) 

200 K

1 atm

29.27 J/(mol K) 

1 bar

29.27 J/(mol K) 

178 K

1 atm

29.31 J/(mol K) 

1 bar

29.31 J/(mol K) 

168 K

1 atm

29.34 J/(mol K) 

1 bar

29.34 J/(mol K) 

158 K

1 atm

29.39 J/(mol K) 

1 bar

29.38 J/(mol K) 

148 K

1 atm

29.44 J/(mol K) 

1 bar

29.44 J/(mol K) 

138 K

1 atm

29.52 J/(mol K) 

1 bar

29.51 J/(mol K) 

128 K

1 atm

29.61 J/(mol K) 

1 bar

29.61 J/(mol K) 

118 K

1 atm

29.73 J/(mol K) 

1 bar

29.72 J/(mol K) 

108 K

1 atm

29.84 J/(mol K) 

1 bar

29.83 J/(mol K) 

98 K

1 atm

29.99 J/(mol K) 

1 bar

29.97 J/(mol K) 

94 K

1 atm

30.23 J/(mol K) 

1 bar

30.21 J/(mol K) 

liquid

90.19 K, 1 atm

54.38 J/(mol K) 

90.06 K, 1 bar

54.37 J/(mol K) 

90 K

1 atm

54.36 J/(mol K) 

1 bar

54.36 J/(mol K) 

82 K

1 atm

53.87 J/(mol K) 

1 bar

53.87 J/(mol K) 

72 K

1 atm

53.69 J/(mol K) 

1 bar

53.69 J/(mol K) 

62 K

1 atm

53.60 J/(mol K) 

1 bar

53.60 J/(mol K) 

56 K

1 atm

53.45 J/(mol K) 

1 bar

53.45 J/(mol K) 

54.37 K

1 atm

53.53 J/(mol K) 

1 bar

53.53 J/(mol K) 

Palladium

298.15 K, 1 bar

25.98 J/(mol K) 

Phosphorus

white phosphorus, 298.15 K, 1 bar

23.824 J/(mol K)

Platinum

298.15 K, 1 bar

25.86 J/(mol K) 

Potassium

298.15 K, 1 bar

29.600 J/(mol K)

Praseodymium

298.15 K, 1 bar

27.20 J/(mol K) 

Radon

298.15 K, 1 bar

20.786 J/(mol K)

Rhenium

298.15 K, 1 bar

25.48 J/(mol K) 

Rhodium

298.15 K, 1 bar

24.98 J/(mol K) 

Rubidium

298.15 K, 1 bar

31.060 J/(mol K)

Ruthenium

298.15 K, 1 bar

24.06 J/(mol K) 

Samarium

298.15 K, 1 bar

29.54 J/(mol K) 

Scandium

298.15 K, 1 bar

25.52 J/(mol K) 

Selenium

298.15 K, 1 bar

25.363 J/(mol K)

Silicon

298.15 K, 1 bar

19.99 J/(mol K) 

Silver

298.15 K, 1 bar

25.350 J/(mol K)

Sodium

298.15 K, 1 bar

28.230 J/(mol K)

Strontium

298.15 K, 1 bar

26.79 J/(mol K) 

Sulfur

α-orthorhombic sulfur, 298.15 K, 1 bar

22.70 J/(mol K) 

Tantalum

298.15 K, 1 bar

25.36 J/(mol K) 

Tellurium

298.15 K, 1 bar

25.73 J/(mol K) 

Terbium

298.15 K, 1 bar

28.91 J/(mol K) 

Thallium

298.15 K, 1 bar

26.32 J/(mol K) 

Thorium

298.15 K, 1 bar

27.32 J/(mol K) 

Thulium

298.15 K, 1 bar

27.03 J/(mol K) 

Tin

gray tin, 298.15 K, 1 bar

25.77 J/(mol K) 

white tin, 298.15 K, 1 bar

26.99 J/(mol K) 

Titanium

298.15 K, 1 bar

25.060 J/(mol K)

Tungsten

298.15 K, 1 bar

24.27 J/(mol K) 

Uranium

crystalline solid, 298.15 K, 1 bar

27.665 J/(mol K)

Vanadium

298.15 K, 1 bar

24.89 J/(mol K) 

Xenon

298.15 K, 1 bar

20.786 J/(mol K)

Ytterbium

298.15 K, 1 bar

26.74 J/(mol K) 

Yttrium

298.15 K, 1 bar

26.53 J/(mol K) 

Zinc

298.15 K, 1 bar

25.390 J/(mol K)

Zirconium

298.15 K, 1 bar

25.36 J/(mol K) 

References    (Click the button next to a value above to see complete citation information for that entry)

Holman, G. J. F., and C. A. ten Seldam. "A Critical Evaluation of the Thermophysical Properties of Mercury." Journal of Physical and Chemical Reference Data, volume 23, number 5, 1994, pp. 807–827.

Lide, David R., editor. CRC Handbook of Chemistry and Physics, 88th edition. Boca Raton, Florida: Taylor & Francis Group, 2008.

Span, Roland, Eric W. Lemmon, Richard T. Jacobsen, Wolfgang Wagner, and Akimichi Yokozeki. "A Reference Equation of State for the Thermodynamic Properties of Nitrogen for Temperatures from 63.151 to 1000 K and Pressures to 2200 MPa." Journal of Physical and Chemical Reference Data, volume 29, number 6, 2000, pp. 1361–1433.

Stewart, Richard B., and Richard T. Jacobsen. "Thermodynamic Properties of Argon from the Triple Point to 1200 K with Pressures to 1000 MPa." Journal of Physical and Chemical Reference Data, volume 18, number 2, 1989, pp. 639–798.

Stewart, Richard B., Richard T. Jacobsen, and w. Wagner. "Thermodynamic Properties of Oxygen from the Triple Point to 300 K with Pressures to 80 MPa." Journal of Physical and Chemical Reference Data, volume 20, number 5, 1991, pp. 917–1021.

Wagman, Donald D., William H. Evans, Vivian B. Parker, Richard H. Schumm, Iva Halow, Sylvia M. Bailey, Kenneth L. Churney, and Ralph L. Nuttall. "Thermal Conductivity of the Elements: A Comprehensive Review." Journal of Physical and Chemical Reference Data, volume 11, supplement 2, 1982, pp. 2–1 to 2–392.

Younglove, B. A. "Thermophysical Properties of Fluids. I. Argon, Ethylene, Parahydrogen, Nitrogen, Nitrogen Trifluoride, and Oxygen." Journal of Physical and Chemical Reference Data, volume 11, supplement 1, 1982, pp. 1–1 to 1–353.